W360

Application Segments

Additive Manufacturing Application

Melting Route

VIGA

Product Description

The BÖHLER W360 AMPO is the powder equivalent of the W360 ISOBLOC. Due to its chemical composition, the material belongs to the product group of hot-work tool steels. After hardening and tempering, it can achieve a hardness of up to 57 HRC with very good toughness properties. Its high temperature wear resistance, heat resistance and toughness characterizes the material. Applications: Printed components with conformal cooling for die casting applications, wear protection layers and repair work in mold making using laser cladding.

Property Features

Particle size distribution 15 – 45 µm:
D10[µm]                            18 – 24
D50[µm]                            29 – 35
D90[µm]                            42 – 50
Apparent density*           ≥ 3.6 g/cm³
Measurement of particle size distribution according to ISO 13322-2 (Dynamic image analysis methods);
* Measurement of apparent density is based on ASTM B964 resp. DIN EN ISO 3923-1 and relates to our typical measured values

 

Achievable mechanical properties of printed part after heat treatment:
Tensile strength (Rm)                            1970 – 2010 MPa
Yield strength (RP₀,₂)                             1500 – 1670 MPa
Elongation (%)                                          6.6 – 8.1
Hardness                                                     55 – 57 HRc
Impact toughness (ISO V)                          8 – 14 J

 

Particle size distribution 45 – 90 µm:
Details on request

Technical Specifications

Material Numbers


BÖHLER patent


Chemical Composition

Chemical composition (average %)
0.50 0.20 0.25 4.50 3.00 0.55

Downloads

Fairs & Events